HIPS
ProsperitiesTestConditionTestMethodValueUnitMeltingFlowRate200°C 5kgISO11335 0g 10minDensityISO11831 04g cm3WaterAbsorptionISO62<
| Prosperities | Test Condition | Test Method | Value | Unit |
| Melting Flow Rate | 200°C/5kg | ISO 1133 | 5.0 | g/10min |
| Density | ISO 1183 | 1.04 | g/cm3 | |
| Water Absorption | ISO 62 | <0.1 | % | |
| Molding Shrinkage | ISO 294 | 0.4-0.7 | % | |
| Tensile Strength | 23°C | ISO 527 | 23 | Mpa |
| Tensile Elongation | 23°C | ISO 527 | 50 | % |
| Flexural Strength | 23°C | ISO 178 | 46 | Mpa |
| Flexural Modulus | 23°C | ISO 178 | 2260 | Mpa |
| Izod Impact Strength | 23°C | ISO 180 | 108 | j/m |
| Rockwell Hardness | 23°C | ASTMD-785 | 65 | L |
| Vicat Softening Temp. | B10/oil | ISO 306 | 95 | °C |
| Heat Distortion Temp. | 1.82Mpa | ISO 75-2 | 79 | °C |
| UL Flame Class Rating | UL 94 | HB | ||
| Residual Monomer | <400 | ppm max |